- 缺口沖擊強度: 1.28
- 拉伸強度 [MPa]: 55.8
- 斷裂伸長率 [%]: 75.8
- 彎曲強度 [MPa]: 37.9
- 彎曲模量 [MPa]: 2.07
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 37.9 MPa | 5500 psi | ASTM D638 |
| Tensile Strength, Yield | 55.8 MPa | 8090 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.17 mm | 2.40 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 421 °F | ASTM D789 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 138 - 216 °C | 280 - 420 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 82.7 - 172 MPa | 12000 - 25000 psi | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |