- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 1.0
- 拉伸強度 [MPa]: 157.0
- 斷裂伸長率 [%]: 220
- 彎曲模量 [MPa]: 8.50
- 硬度: 120.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D786 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 220 MPa | 31900 psi | ASTM D790 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 μm/m-°C @Temperature 20.0 °C | 33.3 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |