- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 2.3
- 拉伸強度 [MPa]: 130.0
- 斷裂伸長率 [%]: 195
- 彎曲模量 [MPa]: 6.80
- 硬度: 119.0
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D786 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 195 MPa | 28300 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm | 4.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |