- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 0.374
- 彎曲模量 [MPa]: 7.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 84.8 MPa | 12300 psi | ISO 527-2 |
| 86.2 MPa | 12500 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 13.8 MPa | 2000 psi | ASTM D790 |
| 13.8 MPa | 2000 psi | ISO 178 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | ISO 178 |
| 7.24 GPa | 1050 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 3.57 kJ/m2 | 1.70 ft-lb/in2 | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 377 °F | Unannealed; ASTM D648 |