- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 0.641
- 彎曲模量 [MPa]: 2.76
- 熱變形溫度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in3 | DAM; ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | 73°F; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 6.0 @Frequency 100 Hz | 6.0 @Frequency 100 Hz | ASTM D150 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in, BK |
| HB | HB | 0.0591 in, NC | |
| HB | HB | 0.118 in, BK | |
| HB | HB | 0.118 in, NC | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |