- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 8.54
- 彎曲模量 [MPa]: 1.55
- 硬度: 105.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 - 0.021 cm/cm | 0.017 - 0.021 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| 52.0 MPa | 7540 psi | ISO 527-2 | |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| 68.9 MPa | 10000 psi | ISO 178 | |
| Flexural Modulus | 1.55 GPa | 225 ksi | ISO 178 |
| 1.76 GPa | 255 ksi | ASTM D790 | |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 861 kJ/m2 | 410 ft-lb/in2 | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ASTM D648 |