- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.8
- 缺口沖擊強(qiáng)度: 5.0
- 拉伸強(qiáng)度 [MPa]: 59.0
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.8 % @Temperature 23.0 °C | 2.8 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 59.0 MPa @Temperature 23.0 °C | 8560 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 84.0 MPa @Temperature 23.0 °C | 12200 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 32 % @Temperature 23.0 °C | 32 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| Dissipation Factor | 0.010 @Frequency 100 Hz, Temperature 23.0 °C | 0.010 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.010 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.010 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 6.00 mm | 266 °F @Thickness 0.236 in | DAM; UL 746B | ||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.710 mm | 167 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 75.0 °C @Thickness 6.00 mm | 167 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 1.50 mm | 167 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.710 mm | 185 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 6.00 mm | 185 °F @Thickness 0.236 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | DAM; UL94 | |||
| Oxygen Index | 24 % | 24 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||