- 密度 [g/cm3]: 1.41
- 缺口沖擊強度: 12.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 35 % | 35 % | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 200 MPa @Temperature 23.0 °C | 29000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 8.40 GPa @Temperature 23.0 °C | 1220 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 11.4 GPa @Temperature 23.0 °C | 1650 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 13.0 kJ/m2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.60 J/cm2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 250 V @Temperature 23.0 °C | 250 V @Temperature 73.4 °F | DAM; UL 746A | ||
| 250 - 400 V @Temperature 23.0 °C | 250 - 400 V @Temperature 73.4 °F | DAM; UL 746A | |||
| 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 125 °C @Thickness 0.710 mm | 257 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF35< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Resin Identification | PA66-GF35 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||