- 密度 [g/cm3]: 1.4
- 缺口沖擊強度: 13.0
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 200 MPa @Temperature 23.0 °C | 29000 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 10.0 GPa @Temperature 23.0 °C | 1450 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 @Temperature -40.0 °C | 6.19 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 15.0 kJ/m2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -40.0 °C | 5.71 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.40 J/cm2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+18 ohm-cm @Temperature 23.0 °C | 2.00e+18 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| Surface Resistance | 4.00e+15 ohm @Temperature 23.0 °C | 4.00e+15 ohm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66-GF35< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Electrical Resins | DAM | |||
| Encapsulation Resins | DAM | ||||
| Glass Reinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-GF35 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||