- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 1.7
- 缺口沖擊強度: 12.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 35 % | 35 % | DAM | ||
| Water Absorption | 1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 5.5 % @Temperature 23.0 °C | 5.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 210 MPa @Temperature 23.0 °C | 30500 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 8.20 GPa @Temperature 23.0 °C | 1190 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 11.3 GPa @Temperature 23.0 °C | 1640 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 15.0 kJ/m2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 6.70 J/cm2 @Temperature -30.0 °C | 31.9 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 7.50 J/cm2 @Temperature -30.0 °C | 35.7 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 8.50 J/cm2 @Temperature 23.0 °C | 40.4 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 9.20 J/cm2 @Temperature 23.0 °C | 43.8 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.60 J/cm2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 8400 MPa @Temperature 23.0 °C | 1.22e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 6000 MPa @Temperature 23.0 °C | 870000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm @Temperature 23.0 °C | 1.00e+11 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.1 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 4.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.014 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.062 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.062 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 85.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF35< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Blow Molding | DAM | |||
| Injection Molding | DAM | ||||
| Product Category | Glass Reinforced Resins | DAM | |||
| Resin Identification | PA66-GF35 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||