- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 1.3
- 成型收縮率 [%]: 0.016
- 缺口沖擊強度: 10.0
- 拉伸強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 2.27
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| 1.3 % @Thickness 1.00 mm, Temperature 23.0 °C | 1.3 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.016 cm/cm @Thickness 3.20 mm | 0.016 in/in @Thickness 0.126 in | Normal; DAM; ASTM D955 | ||
| 0.018 cm/cm @Thickness 3.20 mm | 0.018 in/in @Thickness 0.126 in | Parallel; DAM; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa @Temperature 23.0 °C | 5800 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 5.5 % @Temperature 23.0 °C | 5.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 15 % @Temperature 23.0 °C | 15 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.10 GPa @Temperature 23.0 °C | 160 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 2.27 GPa @Temperature 23.0 °C | 329 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature -40.0 °C | 4.76 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 16.0 kJ/m2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature -30.0 - 30.0 °C | 278 μin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature -30.0 - 30.0 °C | 278 μin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 90.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 50.0 μin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 90.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 90.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 50.0 μin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | |||
| 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 130 μm/m-°C @Temperature 55.0 - 160 °C | 72.2 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| 130 μm/m-°C @Temperature 55.0 - 160 °C | 72.2 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| 290 °C | 554 °F | DAM; Optimum | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | PA66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Toughened Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||