- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.8
- 拉伸強度 [MPa]: 55.0
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.8 % @Temperature 23.0 °C | 2.8 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 85.0 MPa @Temperature 23.0 °C | 12300 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 16 % @Temperature 23.0 °C | 16 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 24 % @Temperature 23.0 °C | 24 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 23 % @Temperature 23.0 °C | 23 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | PA66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||