- 密度 [g/cm3]: 1.14
- 缺口沖擊強度: 0.64
- 拉伸強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | DAM; ASTM D792 | ||
| Density | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 90 % @Temperature 23.0 °C | 90 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.30 GPa @Temperature 23.0 °C | 189 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| 3.03 GPa @Temperature 23.0 °C | 439 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C | 1.20 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature -40.0 °C | 2.86 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 0.550 J/cm2 @Temperature -30.0 °C | 2.62 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 262 °C | 504 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ASTM D648 | ||
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 140 °C @Thickness 0.710 mm | 284 °F @Thickness 0.0280 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 0.710 mm | 203 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 110 °C @Thickness 1.50 mm | 230 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 115 °C @Thickness 0.710 mm | 239 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |||
| 280 - 290 °C | 536 - 554 °F | DAM; Extrusion | |||
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |||
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Extrudable - Coating | Yes | DAM | |||
| Extrudable - Filament | Yes | DAM | |||
| Extrudable - Sheet | Yes | DAM | |||
| Extrudable - Tubing | Yes | DAM | |||
| Features | Heat Aging Resistance, Good | DAM | |||
| Molecular Wt., High | DAM | ||||
| Viscosity, High | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Extrusion | DAM | ||||
| Injection Molding | DAM | ||||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Gears | DAM | |||
| Stock Material for Machining | DAM | ||||