- 缺口沖擊強度: 5.5
- 拉伸強度 [MPa]: 85.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa @Temperature 23.0 °C | 12300 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m2 @Temperature 23.0 °C | 2.62 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 300 kJ/m2 @Temperature 23.0 °C | 143 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Glow Wire Test | 725 °C @Thickness 1.50 mm | 1340 °F @Thickness 0.0591 in | DAM; Ignition; IEC 60695-2-13 | ||
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | DAM; Ignition; IEC 60695-2-13 | |||
| 725 °C @Thickness 0.710 mm | 1340 °F @Thickness 0.0280 in | DAM; Ignition; IEC 60695-2-13 | |||
| 850 °C @Thickness 0.710 mm | 1560 °F @Thickness 0.0280 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | DAM; IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | DAM; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||