- 密度 [g/cm3]: 1.51
- 成型收縮率 [%]: 0.004
- 缺口沖擊強度: 0.32
- 彎曲模量 [MPa]: 8.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | DAM; ASTM D792 | ||
| Density | 1.51 g/cc | 0.0546 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 40 % | 40 % | DAM | ||
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 1.60 mm | 0.0040 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0040 cm/cm @Thickness 3.20 mm | 0.0040 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.0060 cm/cm @Thickness 6.40 mm | 0.0060 in/in @Thickness 0.252 in | Flow; DAM | |||
| 0.0090 cm/cm @Thickness 1.60 mm | 0.0090 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.0090 cm/cm @Thickness 3.20 mm | 0.0090 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.011 cm/cm @Thickness 6.40 mm | 0.011 in/in @Thickness 0.252 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa @Temperature 23.0 °C | 13800 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Strength | 87.0 MPa @Temperature 23.0 °C | 12600 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Modulus | 10.0 GPa @Temperature 23.0 °C | 1450 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Strength | 148 MPa @Temperature 23.0 °C | 21500 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 8.62 GPa @Temperature 23.0 °C | 1250 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 9.50 GPa @Temperature 23.0 °C | 1380 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C | 0.599 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 3.20 J/cm @Temperature 23.0 °C | 5.99 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 2.50 kJ/m2 @Temperature -40.0 °C | 1.19 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 3.50 kJ/m2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 0.200 J/cm2 @Temperature -40.0 °C | 0.952 ft-lb/in2 @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 0.300 J/cm2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 53.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 29.4 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 53.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 29.4 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 66.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 36.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 66.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 36.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 110 μm/m-°C @Temperature 55.0 - 160 °C | 61.1 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| 110 μm/m-°C @Temperature 55.0 - 160 °C | 61.1 μin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 | ||
| 210 °C | 410 °F | DAM; ASTM D648 | |||
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Warpage, Low | DAM | |||
| Filler | Mineral filler | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-MD40< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Low Warp Resins | DAM | |||
| Mineral Reinforced Resins | DAM | ||||
| Resin Identification | PA66-MD40 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Gears | DAM | ||||
| Industrial Applications | DAM | ||||
| Parts, Engineering | DAM | ||||