- 吸水率 [%]: 1.0
- 缺口沖擊強度: 0.374
- 彎曲模量 [MPa]: 4.83
- 硬度: 122.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hours Immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | 1/8 in bar; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | 1/8 in specimen; ASTM D256 |
| Tensile Impact Strength | 126 kJ/m2 | 60.0 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | 0.125 in bar; ASTM D648 |