- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 8.5
- 彎曲強度 [MPa]: 52.4
- 彎曲模量 [MPa]: 1.80
- 硬度: 111.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0145 cm/cm | 0.0145 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 64 | 64 | ASTM D785 |
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Ultimate | 52.4 MPa | 7600 psi | ASTM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Compressive Yield Strength | 66.0 MPa | 9570 psi | ASTM D695 |
| Izod Impact, Notched | 8.50 J/cm | 15.9 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |