- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 1.7
- 彎曲強度 [MPa]: 60.7
- 彎曲模量 [MPa]: 1.90
- 硬度: 112.0
- 熱變形溫度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0125 cm/cm | 0.0125 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 70 | 70 | ASTM D785 |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Ultimate | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Compressive Yield Strength | 76.0 MPa | 11000 psi | ASTM D695 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |