- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.8
- 缺口沖擊強度: 1.1
- 彎曲強度 [MPa]: 186.0
- 彎曲模量 [MPa]: 9.00
- 硬度: 122.0
- 熱變形溫度 [℃]: 249.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 265 MPa | 38400 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Yield Strength | 245 MPa | 35500 psi | ASTM D695 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 263 °C | 505 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 249 °C | >= 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |