- 密度 [g/cm3]: 1.07
- 缺口沖擊強度: 23.0
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 | ||
| Elongation at Break | 45 % | 45 % | Nominal; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 1.90 GPa | 276 ksi | ISO 527 | ||
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 23.0 kJ/m2 @Temperature -40.0 °C | 10.9 ft-lb/in2 @Temperature -40.0 °F | ISO 180 | ||
| 80.0 kJ/m2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | ISO 180 | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 2.80 J/cm2 @Temperature -30.0 °C | 13.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 288 - 305 °C | 550 - 581 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Drying Temperature | 140 °C | 284 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| Descriptive Properties | |||||
| Color | BK 20560 | ||||
| Commercial Status | North America | ||||