- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.3
- 缺口沖擊強度: 2.14
- 彎曲模量 [MPa]: 2.07
- 硬度: 115.0
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 64.1 MPa | 9300 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.3 °C | 164 °F | Unannealed; ASTM D648 |