- 密度 [g/cm3]: 1.08
- 缺口沖擊強度: 83.0
- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 1.703
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 50 % | 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Flexural Modulus | 1.703 GPa | 247.0 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 83.0 kJ/m2 | 39.5 ft-lb/in2 | ISO Test | ||
| 22.0 kJ/m2 @Temperature -40.0 °C | 10.5 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 258 °C | 496 °F | 10 K/min | ||
| 258 °C | 496 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||