- 密度 [g/cm3]: 1.28
- 缺口沖擊強度: 0.53
- 彎曲強度 [MPa]: 162.0
- 彎曲模量 [MPa]: 11.0
- 硬度: 119.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in3 | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 162 MPa | 23500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 239 MPa | 34700 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm | 9.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Approximate middle barrel temperature. |