- 吸水率 [%]: 1.4
- 缺口沖擊強度: 0.98
- 拉伸強度 [MPa]: 118.0
- 彎曲模量 [MPa]: 6.30
- 硬度: 108.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | Wet |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60 | 60 | Wet; ASTM D785 |
| 89 | 89 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 108 | 108 | Wet; ASTM D785 |
| 120 | 120 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 118 MPa | 17100 psi | Wet; ASTM D638 |
| 157 MPa | 22800 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 3.0 % | 3.0 % | Wet; ASTM D638 | |
| Flexural Strength | 177 MPa | 25700 psi | Wet; ASTM D790 |
| 245 MPa | 35500 psi | Dry; ASTM D790 | |
| Flexural Modulus | 6.30 GPa | 914 ksi | Wet; ASTM D790 |
| 8.00 GPa | 1160 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | Dry; ASTM D256 |
| 1.18 J/cm | 2.21 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 9.0 | 9.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 μm/m-°C @Temperature 20.0 °C | 16.7 μin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |