- 吸水率 [%]: 1.4
- 缺口沖擊強度: 0.36
- 拉伸強度 [MPa]: 98.0
- 彎曲模量 [MPa]: 5.80
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | Wet |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | Dry; ASTM D785 |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | Wet; ASTM D638 |
| 128 MPa | 18600 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 3.5 % | 3.5 % | Wet; ASTM D638 | |
| Flexural Strength | 157 MPa | 22800 psi | Wet; ASTM D790 |
| 191 MPa | 27700 psi | Dry; ASTM D790 | |
| Flexural Modulus | 5.80 GPa | 841 ksi | Wet; ASTM D790 |
| 8.80 GPa | 1280 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | Dry; ASTM D256 |
| 0.390 J/cm | 0.731 ft-lb/in | Wet; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Dry; ASTM D648 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA66
- Asahi Kasei Leona? CR302 Nylon 66