- 吸水率 [%]: 1.7
- 缺口沖擊強度: 11.1
- 拉伸強度 [MPa]: 37.0
- 彎曲模量 [MPa]: 1.00
- 硬度: 89.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | Wet |
| Linear Mold Shrinkage | 0.017 - 0.025 cm/cm | 0.017 - 0.025 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 89 | 89 | Wet; ASTM D785 |
| 107 | 107 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | Wet; ASTM D638 |
| 54.0 MPa | 7830 psi | Dry; ASTM D638 | |
| Elongation at Break | 70 % | 70 % | Dry; ASTM D638 |
| 220 % | 220 % | Wet; ASTM D638 | |
| Flexural Strength | 39.0 MPa | 5660 psi | Wet; ASTM D790 |
| 79.0 MPa | 11500 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.00 GPa | 145 ksi | Wet; ASTM D790 |
| 2.00 GPa | 290 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 11.1 J/cm | 20.8 ft-lb/in | Dry; ASTM D256 |
| 13.2 J/cm | 24.7 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 6.0 | 6.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 μm/m-°C @Temperature 20.0 °C | 61.1 μin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Dry; ASTM D648 |