- 密度 [g/cm3]: 1.58
- 缺口沖擊強(qiáng)度: 5.0
- 拉伸強(qiáng)度 [MPa]: 41.0
- 斷裂伸長(zhǎng)率 [%]: 72.0
- 彎曲模量 [MPa]: 3.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 6.4 % | 6.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m2 | 11.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 86.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 47.8 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 107 μm/m-°C @Temperature 23.0 - 60.0 °C | 59.4 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |