- 密度 [g/cm3]: 2.11
- 吸水率 [%]: 1.6
- 缺口沖擊強(qiáng)度: 4.0
- 拉伸強(qiáng)度 [MPa]: 159.0
- 斷裂伸長率 [%]: 207
- 彎曲模量 [MPa]: 14.2
- 熱變形溫度 [℃]: 289.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 g/cc | 0.0762 lb/in3 | ISO 1183 |
| Water Absorption | 1.6 % @Time 86400 sec | 1.6 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 159 MPa | 23100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 19.3 GPa | 2800 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 14.2 GPa | 2060 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m2 | 9.04 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 6.67 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 32.2 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 289 °C | 552 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 281 °C | 538 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |