- 熔體流動速率 [g/10min]: 12.0
- 彎曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ISO 1183 | ||
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 300 °C | 12 g/10 min @Load 4.76 lb, Temperature 572 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 165 MPa | 23900 psi | |||
| Elongation at Yield | 2.2 % | 2.2 % | |||
| 2.6 % | 2.6 % | flexural | |||
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |||
| Flexural Strength | 235 MPa | 34100 psi | |||
| Flexural Modulus | 9.00 GPa | 1310 ksi | |||
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179 1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |||
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| 160 °C | 320 °F | short term | |||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 310 °C | 590 °F | mass temp | ||
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |||
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |||
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |||
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |||
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec | 176 °F @Time 2.00 - 12.0 hour | Vacuum Dryer | ||
| 80.0 °C @Time 7200 - 28800 sec | 176 °F @Time 2.00 - 8.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color (black) | ||||