- 吸水率 [%]: 1.5
- 彎曲模量 [MPa]: 8.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 152 MPa | 22000 psi | |||
| Elongation at Yield | 2.1 % | 2.1 % | |||
| 2.5 % | 2.5 % | flexural | |||
| Modulus of Elasticity | 9.80 GPa | 1420 ksi | |||
| Flexural Strength | 215 MPa | 31200 psi | |||
| Flexural Modulus | 8.50 GPa | 1230 ksi | |||
| Charpy Impact Unnotched | 3.60 J/cm2 | 17.1 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179 1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 35.0 μm/m-°C | 19.4 μin/in-°F | DIN 53752 | ||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| 250 °C | 482 °F | short term | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 310 °C | 590 °F | mass temp | ||
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |||
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |||
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |||
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |||
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec | 176 °F @Time 2.00 - 12.0 hour | Vacuum Dryer | ||
| 80.0 °C @Time 7200 - 28800 sec | 176 °F @Time 2.00 - 8.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | orange | ||||