- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.5
- 缺口沖擊強度: 0.534
- 斷裂伸長率 [%]: 110
- 彎曲模量 [MPa]: 2.83
- 硬度: 119.0
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec | 1.5 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm | 0.010 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength | 93.1 MPa | 13500 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm | 1.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 μm/m-°C | 40.0 μin/in-°F | ASTM D696 |
| Melting Point | 240 °C | 464 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | |