- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 1.5
- 斷裂伸長率 [%]: 150
- 彎曲強度 [MPa]: 95.0
- 彎曲模量 [MPa]: 4.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | Approximate 24 hr. |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Flexural Yield Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
| Izod Impact, Notched | 1.50 J/cm | 2.81 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.790 mm | HB @Thickness 0.0311 in | From Wellman QC Laboratory Testing; UL 94 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 282 - 310 °C | 540 - 590 °F | |
| Middle Barrel Temperature | 277 - 304 °C | 530 - 580 °F | |
| Front Barrel Temperature | 271 - 299 °C | 520 - 570 °F | |
| Nozzle Temperature | 271 - 304 °C | 520 - 580 °F | |
| Melt Temperature | 271 - 304 °C | 520 - 580 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm | |