- 密度 [g/cm3]: 1.06
- 缺口沖擊強度: 55.0
- 拉伸強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 type 1 A | ||
| Elongation at Break | 50 % | 50 % | ISO 527 Type 1A | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 Type 1A | ||
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 55.0 kJ/m2 | 26.2 ft-lb/in2 | ISO 180/1eA | ||
| Charpy Impact, Notched | 5.50 J/cm2 | 26.2 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 | 3.5 | IEC 60250 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | 1210 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |||
| Front Barrel Temperature | 230 - 235 °C | 446 - 455 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 50.0 °C | 122 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 225-230°C | ||||