- 吸水率 [%]: 10.2
- 拉伸強度 [MPa]: 80.0
- 熱變形溫度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | |
| Water Absorption | 10.2 % | 10.2 % | |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | |
| Viscosity Measurement | 205 | 205 | cm3/g Viscosity Number |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 3.40 GPa | 493 ksi | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.580 J/cm2 @Temperature -30.0 °C | 2.76 ft-lb/in2 @Temperature -22.0 °F | |
| 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ||
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+11 ohm-cm | >= 1.00e+11 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 °C | 410 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 70.0 °C @Load 5.10 kg | 158 °F @Load 11.2 lb | 50°C/h |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||