- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.0
- 彎曲模量 [MPa]: 3.70
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183 |
| Water Absorption | 1.0 - 2.0 % | 1.0 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 4.5 - 5.5 % | 4.5 - 5.5 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
| Flexural Strength | 56.0 MPa | 8120 psi | ISO 178 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |