- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 7.0
- 拉伸強度 [MPa]: 40.0
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 75.0 MPa | 10900 psi | conditioned; ISO 2039-1 | ||
| 190 MPa | 27600 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 | |||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | ||
| 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 9.0 % | 9.0 % | dry; ISO 527-1/-2 | ||
| 9.0 % | 9.0 % | dry; ISO 527-1/-2 | |||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 25 % | 25 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.30 GPa | 189 ksi | conditioned; ISO 527-1/-2 | ||
| 3.80 GPa | 551 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 9.00 J/cm2 | 42.8 ft-lb/in2 | dry; ISO 179/1eU | ||
| 7.50 J/cm2 @Temperature 30.0 °C | 35.7 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | dry; ISO 179/1eA | ||
| 0.900 J/cm2 | 4.28 ft-lb/in2 | conditioned; ISO 179/1eA | |||
| 0.300 J/cm2 @Temperature 30.0 °C | 1.43 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 0.350 J/cm2 @Temperature 30.0 °C | 1.67 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Comparative Tracking Index | 575 V | 575 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 | V-0 | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Burning Behaviour | VDE | ||||
| Electricals & Electronics | Cables & Tubes | ||||
| Connectors | |||||
| Electrical appliances | |||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Lighting | |||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||
| Product Attributes | Improved flowability and demoulding | ||||
| Special Characteristics | Flame retardant | ||||