- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.5
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 |
| Water Absorption | 0.50 - 1.5 % | 0.50 - 1.5 % | ISO 62 |
| Water Absorption at Saturation | 3.5 - 4.5 % | 3.5 - 4.5 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.013 cm/cm | 0.0050 - 0.013 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 169 MPa | 24500 psi | ISO 2039-1 |
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 10.44 GPa | 1514 ksi | ISO 527 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.10 J/cm2 | 19.5 ft-lb/in2 | DIN 53453 |
| 3.70 J/cm2 @Temperature -40.0 °C | 17.6 ft-lb/in2 @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 1.10 J/cm2 | 5.24 ft-lb/in2 | DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |