- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.5
- 彎曲模量 [MPa]: 2.60
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 5.5 - 6.5 % | 5.5 - 6.5 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.011 - 0.021 cm/cm | 0.011 - 0.021 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 140 MPa | 20300 psi | ISO 2039-1 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
| 600 V | 600 V | CTI-M 100; IEC 112 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |