- 熔體流動速率 [g/10min]: 258.0
- 密度 [g/cm3]: 1.29
- 缺口沖擊強度: 3.0
- 拉伸強度 [MPa]: 70.0
- 彎曲模量 [MPa]: 3.60
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | ISO 1183 | ||
| Melt Flow | 258 g/10 min @Load 5.00 kg, Temperature 275 °C | 258 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.60 GPa | 522 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 110 MPa | 16000 psi | at max force; ISO 178 | ||
| Flexural Modulus | 3.60 GPa | 522 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | ||
| 3.00 kJ/m2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| 9.00 J/cm2 @Temperature -30.0 °C | 42.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.300 J/cm2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 350 V | 350 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 240 °C | 464 °F | DIN 53765 | ||
| Flammability, UL94 | V-2 @Thickness >=0.400 mm | V-2 @Thickness >=0.0157 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||