- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 0.9
- 斷裂伸長率 [%]: 120
- 彎曲強度 [MPa]: 85.0
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 - 1.50 g/cc | 0.0426 - 0.0542 lb/in3 | Average value: 1.32 g/cc Grade Count:6 |
| Water Absorption | 1.20 % | 1.20 % | Average value: 1.20 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.0120 cm/cm | 0.00200 - 0.0120 in/in | Average value: 0.00650 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 85.0 - 179 MPa | 12300 - 26000 psi | Average value: 126 MPa Grade Count:5 |
| Elongation at Break | 3.00 - 5.00 % | 3.00 - 5.00 % | Average value: 3.63 % Grade Count:6 |
| Flexural Yield Strength | 120 - 240 MPa | 17400 - 34800 psi | Average value: 180 MPa Grade Count:5 |
| Flexural Modulus | 3.80 - 9.31 GPa | 551 - 1350 ksi | Average value: 6.42 GPa Grade Count:6 |
| Izod Impact, Notched | 0.900 - 1.50 J/cm | 1.69 - 2.81 ft-lb/in | Average value: 1.18 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 4.00 - 4.00 J/cm2 @Temperature -20.0 - -20.0 °C | 19.0 - 19.0 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 4.00 J/cm2 Grade Count:1 |
| Charpy Impact, Notched | 0.300 - 0.300 J/cm2 @Temperature -20.0 - -20.0 °C | 1.43 - 1.43 ft-lb/in2 @Temperature -4.00 - -4.00 °F | Average value: 0.300 J/cm2 Grade Count:1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 235 - 262 °C | 455 - 504 °F | Average value: 247 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 - 245 °C | 392 - 473 °F | Average value: 222 °C Grade Count:6 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 310 °C | 482 - 590 °F | Average value: 287 °C Grade Count:3 |
| Mold Temperature | 70.0 - 93.3 °C | 158 - 200 °F | Average value: 81.5 °C Grade Count:3 |
| Drying Temperature | 79.4 - 80.0 °C | 175 - 176 °F | Average value: 79.6 °C Grade Count:3 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.150 % Grade Count:3 |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | Average value: 89.1 MPa Grade Count:3 |