- 密度 [g/cm3]: 1.1
- 拉伸強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 1.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.10 g/cc | 0.0397 lb/in3 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 115 MPa | 16700 psi | ISO 2039/1 | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527 | ||
| Flexural Strength | 47.0 MPa | 6820 psi | ISO 178 | ||
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 185 °C | 365 °F | |||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||