- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.17
- 缺口沖擊強度: 3.0
- 拉伸強度 [MPa]: 35.0
- 斷裂伸長率 [%]: 40.0
- 彎曲強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 - 1.46 g/cc | 0.0419 - 0.0527 lb/in3 | Average value: 1.32 g/cc Grade Count:13 |
| Water Absorption | 1.17 - 9.00 % | 1.17 - 9.00 % | Average value: 5.95 % Grade Count:7 |
| Moisture Absorption at Equilibrium | 2.00 - 3.20 % | 2.00 - 3.20 % | Average value: 2.15 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00400 - 0.0140 cm/cm | 0.00400 - 0.0140 in/in | Average value: 0.00849 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.0140 cm/cm | 0.00600 - 0.0140 in/in | Average value: 0.00970 cm/cm Grade Count:6 |
| Melt Flow | 3.00 - 258 g/10 min | 3.00 - 258 g/10 min | Average value: 204 g/10 min Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 90.0 - 190 MPa | 13100 - 27600 psi | Average value: 144 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 45.0 - 105 MPa | 6530 - 15200 psi | Average value: 69.6 MPa Grade Count:8 |
| Tensile Strength, Yield | 35.0 - 70.0 MPa | 5080 - 10200 psi | Average value: 51.0 MPa Grade Count:5 |
| Elongation at Break | 2.00 - 35.0 % | 2.00 - 35.0 % | Average value: 11.8 % Grade Count:7 |
| Elongation at Yield | 3.40 - 20.0 % | 3.40 - 20.0 % | Average value: 8.42 % Grade Count:7 |
| Modulus of Elasticity | 1.10 - 8.50 GPa | 160 - 1230 ksi | Average value: 4.06 GPa Grade Count:13 |
| Flexural Yield Strength | 40.0 - 110 MPa | 5800 - 16000 psi | Average value: 84.7 MPa Grade Count:6 |
| Flexural Modulus | 1.10 - 3.80 GPa | 160 - 551 ksi | Average value: 2.82 GPa Grade Count:6 |
| Izod Impact, Notched (ISO) | 3.00 - 11.0 kJ/m2 | 1.43 - 5.23 ft-lb/in2 | Average value: 5.81 kJ/m2 Grade Count:7 |
| 3.00 - 3.00 kJ/m2 @Temperature -30.0 - -30.0 °C | 1.43 - 1.43 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 3.00 kJ/m2 Grade Count:2 | |
| Charpy Impact Unnotched | 3.00 - 1000 J/cm2 | 14.3 - 4760 ft-lb/in2 | Average value: 6.97 J/cm2 Grade Count:12 |
| 3.00 - 9.00 J/cm2 @Temperature -30.0 - 30.0 °C | 14.3 - 42.8 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 5.24 J/cm2 Grade Count:7 | |
| Charpy Impact, Notched | 0.300 - 3.50 J/cm2 | 1.43 - 16.7 ft-lb/in2 | Average value: 0.692 J/cm2 Grade Count:12 |
| 0.200 - 0.500 J/cm2 @Temperature -30.0 - 30.0 °C | 0.952 - 2.38 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 0.341 J/cm2 Grade Count:7 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+15 ohm-cm | 1.00e+9 - 1.00e+15 ohm-cm | Average value: 8.10e+13 ohm-cm Grade Count:7 |
| Surface Resistance | 1.00e+10 - 1.00e+11 ohm | 1.00e+10 - 1.00e+11 ohm | Average value: 7.00e+10 ohm Grade Count:6 |
| Dielectric Strength | 21.0 - 34.0 kV/mm | 533 - 864 kV/in | Average value: 27.3 kV/mm Grade Count:3 |
| Comparative Tracking Index | 350 - 600 V | 350 - 600 V | Average value: 453 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 - 90.0 μm/m-°C | 22.2 - 50.0 μin/in-°F | Average value: 72.0 μm/m-°C Grade Count:5 |
| CTE, linear, Transverse to Flow | 60.0 - 100 μm/m-°C | 33.3 - 55.6 μin/in-°F | Average value: 80.0 μm/m-°C Grade Count:5 |
| Melting Point | 222 - 260 °C | 432 - 500 °F | Average value: 247 °C Grade Count:13 |
| Maximum Service Temperature, Air | 80.0 - 220 °C | 176 - 428 °F | Average value: 148 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 - 220 °C | 194 - 428 °F | Average value: 128 °C Grade Count:7 |
| Deflection Temperature at 8.0 MPa | 60.0 - 70.0 °C | 140 - 158 °F | Average value: 65.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 310 °C | 482 - 590 °F | Average value: 266 °C Grade Count:6 |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Average value: 77.1 °C Grade Count:7 |