- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.007
- 缺口沖擊強度: 0.801
- 斷裂伸長率 [%]: 45.0
- 彎曲強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 8.62
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 - 1.62 g/cc | 0.0502 - 0.0585 lb/in3 | Average value: 1.50 g/cc Grade Count:37 |
| Filler Content | 40.0 - 43.0 % | 40.0 - 43.0 % | Average value: 41.5 % Grade Count:4 |
| Water Absorption | 0.00700 - 6.00 % | 0.00700 - 6.00 % | Average value: 3.96 % Grade Count:28 |
| Moisture Absorption at Equilibrium | 1.00 - 2.00 % | 1.00 - 2.00 % | Average value: 1.65 % Grade Count:22 |
| Water Absorption at Saturation | 4.00 - 5.00 % | 4.00 - 5.00 % | Average value: 4.38 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00100 - 0.0180 cm/cm | 0.00100 - 0.0180 in/in | Average value: 0.00213 cm/cm Grade Count:28 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.0110 cm/cm | 0.00300 - 0.0110 in/in | Average value: 0.00513 cm/cm Grade Count:24 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 100 - 325 MPa | 14500 - 47100 psi | Average value: 223 MPa Grade Count:21 |
| Tensile Strength, Ultimate | 50.0 - 265 MPa | 7250 - 38400 psi | Average value: 188 MPa Grade Count:37 |
| 140 - 150 MPa @Temperature 80.0 - 80.0 °C | 20300 - 21800 psi @Temperature 176 - 176 °F | Average value: 120 MPa Grade Count:4 | |
| 100 - 115 MPa @Temperature 110 - 150 °C | 14500 - 16700 psi @Temperature 230 - 302 °F | Average value: 120 MPa Grade Count:2 | |
| 100 - 115 MPa @Time 1.80e+7 - 7.20e+7 sec | 14500 - 16700 psi @Time 5000 - 20000 hour | Average value: 120 MPa Grade Count:2 | |
| Elongation at Break | 1.50 - 16.0 % | 1.50 - 16.0 % | Average value: 3.54 % Grade Count:36 |
| 2.40 - 2.80 % @Temperature 80.0 - 80.0 °C | 2.40 - 2.80 % @Temperature 176 - 176 °F | Average value: 2.70 % Grade Count:4 | |
| Elongation at Yield | 3.00 - 6.00 % | 3.00 - 6.00 % | Average value: 4.60 % Grade Count:3 |
| Modulus of Elasticity | 3.00 - 17.8 GPa | 435 - 2580 ksi | Average value: 12.2 GPa Grade Count:33 |
| 8.05 - 10.0 GPa @Temperature 80.0 - 80.0 °C | 1170 - 1450 ksi @Temperature 176 - 176 °F | Average value: 8.63 GPa Grade Count:4 | |
| Flexural Yield Strength | 45.0 - 380 MPa | 6530 - 55100 psi | Average value: 290 MPa Grade Count:12 |
| 240 - 260 MPa @Temperature 80.0 - 80.0 °C | 34800 - 37700 psi @Temperature 176 - 176 °F | Average value: 253 MPa Grade Count:4 | |
| Flexural Modulus | 8.62 - 15.0 GPa | 1250 - 2180 ksi | Average value: 12.5 GPa Grade Count:11 |
| 8.30 - 9.50 GPa @Temperature 80.0 - 80.0 °C | 1200 - 1380 ksi @Temperature 176 - 176 °F | Average value: 9.10 GPa Grade Count:3 | |
| Izod Impact, Notched | 0.801 - 1.80 J/cm | 1.50 - 3.37 ft-lb/in | Average value: 1.45 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 8.50 - 22.0 kJ/m2 | 4.04 - 10.5 ft-lb/in2 | Average value: 16.4 kJ/m2 Grade Count:4 |
| Izod Impact, Unnotched (ISO) | 57.0 - 82.0 kJ/m2 | 27.1 - 39.0 ft-lb/in2 | Average value: 70.3 kJ/m2 Grade Count:3 |
| 48.0 - 74.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 22.8 - 35.2 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 62.3 kJ/m2 Grade Count:3 | |
| Charpy Impact Unnotched | 4.00 J/cm2 - NB | 19.0 ft-lb/in2 - NB | Average value: 8.07 J/cm2 Grade Count:32 |
| 3.00 J/cm2 - NB @Temperature -40.0 - 30.0 °C | 14.3 ft-lb/in2 - NB @Temperature -40.0 - 86.0 °F | Average value: 6.92 J/cm2 Grade Count:27 | |
| Charpy Impact, Notched | 0.400 - 4.50 J/cm2 | 1.90 - 21.4 ft-lb/in2 | Average value: 2.01 J/cm2 Grade Count:32 |
| 0.300 - 4.50 J/cm2 @Temperature -30.0 - 30.0 °C | 1.43 - 21.4 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 1.90 J/cm2 Grade Count:25 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 1.00e+15 ohm-cm | 1.00e+11 - 1.00e+15 ohm-cm | Average value: 1.33e+14 ohm-cm Grade Count:24 |
| Surface Resistance | 1.00e+10 - 1.00e+13 ohm | 1.00e+10 - 1.00e+13 ohm | Average value: 1.37e+12 ohm Grade Count:19 |
| Dielectric Strength | 18.5 - 45.0 kV/mm | 470 - 1140 kV/in | Average value: 27.9 kV/mm Grade Count:22 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 553 V Grade Count:24 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 - 30.0 μm/m-°C | 5.56 - 16.7 μin/in-°F | Average value: 19.4 μm/m-°C Grade Count:25 |
| CTE, linear, Transverse to Flow | 50.0 - 100 μm/m-°C | 27.8 - 55.6 μin/in-°F | Average value: 75.2 μm/m-°C Grade Count:22 |
| Melting Point | 235 - 310 °C | 455 - 590 °F | Average value: 258 °C Grade Count:36 |
| Maximum Service Temperature, Air | 90.0 - 250 °C | 194 - 482 °F | Average value: 164 °C Grade Count:23 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 - 257 °C | 428 - 495 °F | Average value: 239 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 - 280 °C | 293 - 536 °F | Average value: 232 °C Grade Count:35 |
| Deflection Temperature at 8.0 MPa | 60.0 - 235 °C | 140 - 455 °F | Average value: 192 °C Grade Count:25 |
| Flammability, UL94 | HB | HB | Grade Count:24 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 70.0 - 120 °C | 158 - 248 °F | Average value: 90.0 °C Grade Count:6 |
| Feed Temperature | 20.0 - 80.0 °C | 68.0 - 176 °F | Average value: 41.4 °C Grade Count:7 |
| Die Temperature | 310 - 320 °C | 590 - 608 °F | Average value: 315 °C Grade Count:6 |
| Melt Temperature | 271 - 325 °C | 520 - 617 °F | Average value: 296 °C Grade Count:8 |
| Mold Temperature | 71.1 - 120 °C | 160 - 248 °F | Average value: 95.7 °C Grade Count:3 |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Average value: 76.2 °C Grade Count:8 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 3.38 hour Grade Count:8 |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.153 % Grade Count:7 |
| Injection Pressure | 34.5 - 150 MPa | 5000 - 21800 psi | Average value: 125 MPa Grade Count:8 |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | Average value: 63.6 MPa Grade Count:7 |
| Back Pressure | 0.345 - 3.00 MPa | 50.0 - 435 psi | Average value: 2.42 MPa Grade Count:8 |
| Screw Speed | 25.0 - 120 rpm | 25.0 - 120 rpm | Average value: 38.7 rpm Grade Count:7 |
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | Average value: 308 °C Grade Count:6 |