- 吸水率 [%]: 1.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 50 % | 50 % | ISO 1172 |
| Water Absorption | 1.05 % @Temperature 23.0 °C | 1.05 % @Temperature 73.4 °F | 50% r.h.; ISO 62 |
| Water Absorption at Saturation | 3.5 - 4.0 % | 3.5 - 4.0 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 220 MPa | 31900 psi | 5 [mm/min]; ISO 527-1/2 |
| 110 MPa @Temperature 140 - 150 °C, Time 1.80e+7 sec | 16000 psi @Temperature 284 - 302 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| 110 MPa @Temperature 110 - 130 °C, Time 7.20e+7 sec | 16000 psi @Temperature 230 - 266 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 16.5 GPa | 2390 ksi | 1[mm/min]; ISO 527-1/2 |
| Charpy Impact Unnotched | 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 1.70 J/cm2 @Temperature 23.0 °C | 8.09 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ISO 11357-1, DSC,10 [K/min] |