- 密度 [g/cm3]: 2.0
- 拉伸強度 [MPa]: 13.8
- 彎曲強度 [MPa]: 3.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 - 2.65 g/cc | 0.0723 - 0.0957 lb/in3 | Average value: 2.14 g/cc Grade Count:21 |
| Particle Size | 25.0 - 800 μm | 25.0 - 800 μm | Average value: 505 μm Grade Count:4 |
| Deformation | 0.300 - 10.6 % | 0.300 - 10.6 % | Average value: 4.05 % Grade Count:15 |
| 1.30 - 9.00 % @Time 86400 - 86400 sec | 1.30 - 9.00 % @Time 24.0 - 24.0 hour | Average value: 4.32 % Grade Count:2 | |
| 1.30 - 9.00 % @Pressure 0.981 - 4.90 MPa | 1.30 - 9.00 % @Pressure 142 - 711 psi | Average value: 4.32 % Grade Count:2 | |
| 1.30 - 9.00 % @Temperature 150 - 150 °C | 1.30 - 9.00 % @Temperature 302 - 302 °F | Average value: 4.32 % Grade Count:2 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58.0 - 70.0 | 58.0 - 70.0 | Average value: 62.5 Grade Count:12 |
| Ball Indentation Hardness | 38.0 - 56.0 MPa | 5510 - 8120 psi | Average value: 50.3 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 3.00 - 27.6 MPa | 435 - 4000 psi | Average value: 16.6 MPa Grade Count:19 |
| Tensile Strength, Yield | 13.8 - 16.7 MPa | 2000 - 2420 psi | Average value: 14.9 MPa Grade Count:3 |
| Elongation at Break | 3.00 - 350 % | 3.00 - 350 % | Average value: 169 % Grade Count:22 |
| Compressive Yield Strength | 6.86 - 16.0 MPa | 996 - 2320 psi | Average value: 9.98 MPa Grade Count:7 |
| Shear Strength | 10.3421 - 15.8579 MPa @Temperature 26.7 - 204 °C | 1500.00 - 2300.00 psi @Temperature 80.0 - 400 °F | Average value: 12.5 MPa Grade Count:1 |
| Coefficient of Friction | 0.0800 - 0.160 | 0.0800 - 0.160 | Average value: 0.123 Grade Count:11 |
| Coefficient of Friction, Static | 0.0800 - 0.300 | 0.0800 - 0.300 | Average value: 0.142 Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.00e+7 ohm-cm | 100 - 1.00e+7 ohm-cm | Average value: 1.82e+6 ohm-cm Grade Count:11 |
| Surface Resistance | 1000 - 1.00e+7 ohm | 1000 - 1.00e+7 ohm | Average value: 1.20e+6 ohm Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 - 150 μm/m-°C | 41.7 - 83.3 μin/in-°F | Average value: 108 μm/m-°C Grade Count:3 |
| 100 - 223.2 μm/m-°C @Temperature 30.0 - 300 °C | 55.6 - 124.0 μin/in-°F @Temperature 86.0 - 572 °F | Average value: 156 μm/m-°C Grade Count:2 | |
| Thermal Conductivity | 0.260 - 0.988 W/m-K | 1.80 - 6.86 BTU-in/hr-ft2-°F | Average value: 0.527 W/m-K Grade Count:11 |
| 0.290 - 0.310 W/m-K @Temperature 100 - 250 °C | 2.01 - 2.15 BTU-in/hr-ft2-°F @Temperature 212 - 482 °F | Average value: 0.300 W/m-K Grade Count:1 | |
| Melting Point | 327 °C | 621 °F | Average value: 327 °C Grade Count:7 |
| Maximum Service Temperature, Air | 260 - 270 °C | 500 - 518 °F | Average value: 263 °C Grade Count:10 |
| Minimum Service Temperature, Air | -260 - -50.0 °C | -436 - -58.0 °F | Average value: -131 °C Grade Count:10 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:7 |