- 密度 [g/cm3]: 1.4
- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 16.0
- 斷裂伸長率 [%]: 5.50
- 彎曲強度 [MPa]: 6.89
- 彎曲模量 [MPa]: 0.490
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 - 3.10 g/cc | 0.0506 - 0.112 lb/in3 | Average value: 2.24 g/cc Grade Count:75 |
| Apparent Bulk Density | 0.500 - 0.820 g/cc | 0.0181 - 0.0296 lb/in3 | Average value: 0.663 g/cc Grade Count:6 |
| Water Absorption | 0.000 - 0.100 % | 0.000 - 0.100 % | Average value: 0.0379 % Grade Count:19 |
| Moisture Absorption at Equilibrium | 0.0200 - 0.220 % | 0.0200 - 0.220 % | Average value: 0.0720 % Grade Count:5 |
| 0.0100 - 0.0500 % @Temperature 50.0 - 50.0 °C | 0.0100 - 0.0500 % @Temperature 122 - 122 °F | Average value: 0.0300 % Grade Count:2 | |
| 0.0100 - 0.0500 % @Time 173000 - 173000 sec | 0.0100 - 0.0500 % @Time 48.0 - 48.0 hour | Average value: 0.0300 % Grade Count:2 | |
| Particle Size | 25.0 - 800 μm | 25.0 - 800 μm | Average value: 535 μm Grade Count:14 |
| Viscosity | 1.00e+13 - 1.00e+15 cP @Temperature 340 - 380 °C | 1.00e+13 - 1.00e+15 cP @Temperature 644 - 716 °F | Average value: 5.05e+14 cP Grade Count:10 |
| Permeability | 0.0150 | 0.0150 | Average value: 0.0150 Grade Count:4 |
| Thickness | 70.0 - 3180 microns | 2.76 - 125 mil | Average value: 821 microns Grade Count:17 |
| Linear Mold Shrinkage | 0.0160 - 0.0500 cm/cm | 0.0160 - 0.0500 in/in | Average value: 0.0300 cm/cm Grade Count:15 |
| Deformation | 1.00 - 30.0 % | 1.00 - 30.0 % | Average value: 7.75 % Grade Count:39 |
| 0.260 - 2.10 % @Temperature 50.0 - 150 °C | 0.260 - 2.10 % @Temperature 122 - 302 °F | Average value: 5.86 % Grade Count:3 | |
| 0.260 - 2.10 % @Pressure 7.00 - 14.0 MPa | 0.260 - 2.10 % @Pressure 1020 - 2030 psi | Average value: 5.86 % Grade Count:3 | |
| 2.60 - 19.0 % @Pressure 0.981 - 4.90 MPa | 2.60 - 19.0 % @Pressure 142 - 711 psi | Average value: 5.86 % Grade Count:2 | |
| 2.60 - 19.0 % @Time 86400 - 86400 sec | 2.60 - 19.0 % @Time 24.0 - 24.0 hour | Average value: 5.86 % Grade Count:2 | |
| 2.60 - 19.0 % @Temperature 150 - 150 °C | 2.60 - 19.0 % @Temperature 302 - 302 °F | Average value: 5.86 % Grade Count:2 | |
| Coating Weight | 130 - 630 g/m2 | 81.3 - 394 lb/ream | Average value: 354 g/m2 Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50.0 - 68.0 | 50.0 - 68.0 | Average value: 60.0 Grade Count:49 |
| Ball Indentation Hardness | 29.0 - 60.0 MPa | 4210 - 8700 psi | Average value: 42.4 MPa Grade Count:11 |
| Tensile Strength, Ultimate | 6.89 - 50.0 MPa | 1000 - 7250 psi | Average value: 20.3 MPa Grade Count:68 |
| 18.0 - 34.0 MPa @Temperature 100 - 100 °C | 2610 - 4930 psi @Temperature 212 - 212 °F | Average value: 26.5 MPa Grade Count:2 | |
| Tensile Strength, Yield | 16.0 - 23.5 MPa | 2320 - 3410 psi | Average value: 19.2 MPa Grade Count:6 |
| Elongation at Break | 4.00 - 450 % | 4.00 - 450 % | Average value: 226 % Grade Count:70 |
| 5.80 - 8.70 % @Temperature 100 - 100 °C | 5.80 - 8.70 % @Temperature 212 - 212 °F | Average value: 7.57 % Grade Count:2 | |
| Modulus of Elasticity | 0.0931 - 4.32 GPa | 13.5 - 627 ksi | Average value: 1.36 GPa Grade Count:26 |
| 0.379212 - 0.489528 GPa @Temperature 100 - 100 °C | 55.0009 - 71.0011 ksi @Temperature 212 - 212 °F | Average value: 0.438 GPa Grade Count:2 | |
| Flexural Yield Strength | 5.50 - 38.0 MPa | 798 - 5510 psi | Average value: 20.6 MPa Grade Count:8 |
| Flexural Modulus | 0.490 - 4.36 GPa | 71.1 - 633 ksi | Average value: 1.26 GPa Grade Count:14 |
| Compressive Yield Strength | 0.785 - 54.0 MPa | 114 - 7830 psi | Average value: 16.0 MPa Grade Count:34 |
| 1.80 - 43.0 MPa @Temperature 100 - 150 °C | 261 - 6240 psi @Temperature 212 - 302 °F | Average value: 21.8 MPa Grade Count:4 | |
| 1.80 - 43.0 MPa @Strain 0.200 - 17.6 % | 261 - 6240 psi @Strain 0.200 - 17.6 % | Average value: 21.8 MPa Grade Count:4 | |
| Compressive Modulus | 0.430 - 2.14 GPa | 62.4 - 311 ksi | Average value: 0.939 GPa Grade Count:8 |
| 0.500 - 0.860 GPa @Temperature 100 - 100 °C | 72.5 - 125 ksi @Temperature 212 - 212 °F | Average value: 0.622 GPa Grade Count:2 | |
| Shear Strength | 14.479 - 19.9948 MPa @Temperature 26.7 - 149 °C | 2100.0 - 2900.00 psi @Temperature 80.0 - 300 °F | Average value: 17.4 MPa Grade Count:1 |
| Izod Impact, Notched | 1.10 - 1.37 J/cm | 2.06 - 2.57 ft-lb/in | Average value: 1.24 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 1.60 J/cm | 3.00 ft-lb/in | Average value: 1.60 J/cm Grade Count:10 |
| Coefficient of Friction | 0.0600 - 0.360 | 0.0600 - 0.360 | Average value: 0.160 Grade Count:32 |
| Coefficient of Friction, Static | 0.0200 - 0.270 | 0.0200 - 0.270 | Average value: 0.0933 Grade Count:26 |
| Tear Strength | 12.0 - 71.0 kN/m | 68.5 - 405 pli | Average value: 33.9 kN/m Grade Count:5 |
| Peel Strength | 0.701 - 5.47 kN/m | 4.00 - 31.2 pli | Average value: 2.39 kN/m Grade Count:11 |
| 1.38487 - 1.84065 kN/m @Temperature 288 - 288 °C | 7.90207 - 10.5027 pli @Temperature 550 - 550 °F | Average value: 1.67 kN/m Grade Count:3 | |
| 1.38487 - 1.84065 kN/m @Time 10.0 - 20.0 sec | 7.90207 - 10.5027 pli @Time 0.00278 - 0.00556 hour | Average value: 1.67 kN/m Grade Count:3 | |
| K (wear) Factor | 10.0 - 142 x 10-8 mm3/N-M | 4.96 - 70.6 x 10-10 in3-min/ft-lb-hr | Average value: 39.6 x 10-8 mm3/N-M Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 1.00e+18 ohm-cm | 10000 - 1.00e+18 ohm-cm | Average value: 1.87e+17 ohm-cm Grade Count:44 |
| Surface Resistance | 1000 - 1.00e+16 ohm | 1000 - 1.00e+16 ohm | Average value: 1.30e+15 ohm Grade Count:33 |
| Dielectric Constant | 1.92 - 11.2 | 1.92 - 11.2 | Average value: 3.94 Grade Count:28 |
| Dielectric Strength | 3.00 - 37.0 kV/mm | 76.2 - 940 kV/in | Average value: 18.3 kV/mm Grade Count:24 |
| 11.8504 - 12.5197 kV/mm @Temperature 121 - 121 °C | 300.999 - 317.999 kV/in @Temperature 250 - 250 °F | Average value: 12.2 kV/mm Grade Count:2 | |
| 11.8504 - 12.5197 kV/mm @Time 10800 - 10800 sec | 300.999 - 317.999 kV/in @Time 3.00 - 3.00 hour | Average value: 12.2 kV/mm Grade Count:2 | |
| Dissipation Factor | 0.0000100 - 0.420 | 0.0000100 - 0.420 | Average value: 0.0225 Grade Count:26 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 - 237 μm/m-°C | 6.11 - 132 μin/in-°F | Average value: 74.8 μm/m-°C Grade Count:41 |
| 50.0 - 171 μm/m-°C @Temperature 25.6 - 300 °C | 27.8 - 95.0 μin/in-°F @Temperature 78.0 - 572 °F | Average value: 110 μm/m-°C Grade Count:11 | |
| CTE, linear, Transverse to Flow | 99.1 - 99.1 μm/m-°C @Temperature 26.0 - 200 °C | 55.1 - 55.1 μin/in-°F @Temperature 78.8 - 392 °F | Average value: 99.1 μm/m-°C Grade Count:1 |
| Specific Heat Capacity | 0.790 - 1.00 J/g-°C | 0.189 - 0.239 BTU/lb-°F | Average value: 0.910 J/g-°C Grade Count:12 |
| Thermal Conductivity | 0.220 - 0.558 W/m-K | 1.53 - 3.87 BTU-in/hr-ft2-°F | Average value: 0.338 W/m-K Grade Count:28 |
| 0.200 - 1.44 W/m-K @Temperature 80.0 - 250 °C | 1.39 - 9.99 BTU-in/hr-ft2-°F @Temperature 176 - 482 °F | Average value: 0.480 W/m-K Grade Count:18 | |
| Melting Point | 327 °C | 621 °F | Average value: 327 °C Grade Count:24 |
| Maximum Service Temperature, Air | 230 - 316 °C | 446 - 601 °F | Average value: 263 °C Grade Count:42 |
| Minimum Service Temperature, Air | -268 - -20.0 °C | -450 - -4.00 °F | Average value: -171 °C Grade Count:29 |
| Decomposition Temperature | 500 °C | 932 °F | Average value: 500 °C Grade Count:11 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:36 |
| Oxygen Index | 95.0 - 100 % | 95.0 - 100 % | Average value: 95.7 % Grade Count:12 |
| Shrinkage | 1.60 - 2.80 % | 1.60 - 2.80 % | Average value: 2.08 % Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Average value: 370 °C Grade Count:3 |
| Back Pressure | 30.0 - 70.0 MPa | 4350 - 10200 psi | Average value: 45.0 MPa Grade Count:3 |