- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.8
- 拉伸強度 [MPa]: 34.0
- 斷裂伸長率 [%]: 55.0
- 彎曲強度 [MPa]: 35.0
- 彎曲模量 [MPa]: 1.73
- 脆化溫度 [℃]: -30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 - 1.79 g/cc | 0.0639 - 0.0647 lb/in3 | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | ASTM D570 |
| Linear Mold Shrinkage | 0.025 - 0.030 cm/cm | 0.025 - 0.030 in/in | |
| Melt Flow | 8.0 - 10 g/10 min @Load 3.80 kg | 8.0 - 10 g/10 min @Load 8.38 lb | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 76 - 80 | 76 - 80 | ASTM D2240 |
| Tensile Strength, Ultimate | 35.0 - 45.0 MPa | 5080 - 6530 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 - 48.0 MPa | 4930 - 6960 psi | ASTM D638 |
| Elongation at Break | 50 - 250 % | 50 - 250 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 1.70 - 3.10 GPa | 247 - 450 ksi | ASTM D638 |
| Flexural Yield Strength | 55.0 - 76.0 MPa | 7980 - 11000 psi | ASTM D790 |
| Flexural Modulus | 1.73 - 2.41 GPa | 251 - 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 - 1.30 J/cm | 1.50 - 2.44 ft-lb/in | |
| Izod Impact, Unnotched | >= 15.0 J/cm | >= 28.1 ft-lb/in | Low Temp; ASTM D256 |
| Coefficient of Friction, Dynamic | 0.12 - 0.15 | 0.12 - 0.15 | ASTM D1894 |
| Coefficient of Friction, Static | 0.10 - 0.15 | 0.10 - 0.15 | ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.25e+15 ohm-cm | 1.25e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.6 @Frequency 1e+6 Hz | 5.6 @Frequency 1e+6 Hz | ASTM D150 |
| 6.9 @Frequency 60 Hz | 6.9 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 13.0 kV/mm @Thickness 3.20 mm | 330 kV/in @Thickness 0.126 in | Short-Time 500 V/sec |
| Dissipation Factor | 0.035 @Frequency 60 Hz | 0.035 @Frequency 60 Hz | ASTM D150 |
| 0.158 @Frequency 1e+6 Hz | 0.158 @Frequency 1e+6 Hz | ASTM D150 | |
| Arc Resistance | >= 50 sec | >= 50 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 - 120 μm/m-°C @Temperature 20.0 °C | 55.6 - 66.7 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.190 - 0.220 W/m-K | 1.32 - 1.53 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 165 - 168 °C | 329 - 334 °F | ASTM D3418 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | No oxidative or thermal degradation after 5 years at 150°C (300°F) |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | TMA |
| Brittleness Temperature | <= -30.0 °C | <= -22.0 °F | ASTM D2236 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.42 | 1.42 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 215 - 232 °C | 419 - 450 °F | Preheat |