- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.04
- 缺口沖擊強度: 4.27
- 拉伸強度 [MPa]: 34.5
- 斷裂伸長率 [%]: 46.9
- 彎曲模量 [MPa]: 1.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Tensile Modulus | 0.862 GPa | 125 ksi | ASTM D638 |
| Flexural Yield Strength | 46.9 MPa | 6800 psi | ASTM D790 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 7.5 @Frequency 1000 Hz | 7.5 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 10.6 kV/mm | 270 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 μm/m-°C @Temperature 20.0 °C | 78.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 157 °C | 315 °F | ASTM D4591 |
| Maximum Service Temperature, Air | 116 °C | 240 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.7 °C | 125 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 42 % | 42 % | ASTM D2863 |