- 密度 [g/cm3]: 1.84
- 缺口沖擊強(qiáng)度: 0.55
- 斷裂伸長(zhǎng)率 [%]: 108
- 彎曲模量 [MPa]: 11.87
- 熱變形溫度 [℃]: 166.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D792 |
| Density | 1.84 g/cc | 0.0665 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
| 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.46 GPa | 2097 ksi | 1 mm/min; ISO 527 |
| 15.78 GPa | 2289 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Yield Strength | 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.87 GPa | 1722 ksi | 2 mm/min; ISO 178 |
| 12.5 GPa | 1810 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.01 J/cm | 3.77 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m2 | 6.19 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C | 9.59 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.44 | 0.44 | ASTM D3702 Modified |
| K (wear) Factor | 8.06 x 10-8 mm3/N-M | 4.00 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 21.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 11.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 46.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 168 °C @Thickness 3.20 mm | 334 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 164 °C @Thickness 3.20 mm | 327 °F @Thickness 0.126 in | unannealed; ASTM D648 | |