- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.95
- 缺口沖擊強度: 0.85
- 拉伸強度 [MPa]: 58.0
- 彎曲模量 [MPa]: 6.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in3 | DIN 53479 |
| Water Absorption | >= 0.040 % | >= 0.040 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 7.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | ASTM-D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM-D638 |
| Tensile Modulus | 1.10 GPa | 160 ksi | ASTM-D790 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM-D790 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C | 1.59 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | |